Aluminum 6061-T6 has a minimum yield strength of 35 ksi (240 MPa), which is almost equal to that of A36 steel. This strength, combined with its light weight (about 1/3 that of steel), makes it particularly suitable for structural applications where static loads are a
Aluminum 6061-T6; 6061-T651. Subcategory: 6000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal. Close Analogs: Combines relatively high strength, good workability, and high resistance to corrosion; widely available. The T8 and T9 tempers offer better chipping characteristics over the T6
Two critical strength measures for 6061-T6 aluminum are yield strength and ultimate strength. The yield strength, which is the maximum stress the material can endure while remaining elastically deformed, is 276 MPa (40,000 psi). In comparison, the ultimate tensile strength, or the maximum stress the material can withstand before fracturing, is
6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. ( 550 C) in a cooled die, leaving a part in W-temper condition before artificial aging to the T6 full strength state. Forgings. 6061 is an alloy
Aluminum 6061-T6 is the one of the most common types of aluminum metals used in the industrial world today. With its high strength-to-weight ratio and excellent mability, it is perfect for applications in aerospace, transportation equipment and construction materials manufacturing. Aluminum 6061-T6 is generally heat treated and
This alloy is renowned for its excellent mechanical properties. 6061 T6 aluminum has a yield strength of 276 MPa, tensile strength of 310 MPa, and a shear strength of 207 MPa. Its elastic modulus is 68.9 GPa, with a fatigue strength of 96.5 MPa, Poisson\'s ratio of 0.33, and Brinell hardness of 95. The elongation at break ranges from 12 -
Material Properties and specifications of 6061 Aluminium material. 6061 : T6 : 42 ksi: 35 ksi: 32 ksi: 25 ksi: 21 ksi: 10,100 ksi: 0.33 : 168 lb/ft 3: non_welded : B632, tread plate Material Properties . Unit System Thickness Range Alloy Temper Ultimate Tensile Strength, F tu Yield Strength, F ty Compressive Yield Strength, F cy Ultimate
Aluminum 6061-T6; 6061-T651 Categories: Metal; Nonferrous Metal; Aluminum Alloy; 6000 Series Aluminum Alloy Material Tensile Strength, Ultimate 310 MPa 45000 psi AA; Typical 24.0 MPa Temperature 371 °C 3480 psi Temperature .0 MPa Temperature 316 °C 4640 psi Temperature 601
6061-T6 aluminum properties include its structural strength and toughness. 6061 T6 aluminum is commonly used in aircraft construction. clear and color dye, and hardcoat. 6061 aluminum alloy is also easily welded and joined. However, in its -T6 condition the welds may lose some strength, which can be restored by re-heat-treating and
The high strength of 6061 T6 aluminum ensures the structural integrity of these components while reducing the overall weight of the vehicle. This weight reduction contributes to better fuel efficiency and enhanced performance. Furthermore, 6061 T6 aluminum\'s resistance to corrosion is crucial in automotive applications, as vehicles are often
From prototype to production, get custom parts at consistently low prices. Get instant pricing on CNC machined metal or plastic parts in over 40 certified
Browse Auto Parts Accessories by category type and find the parts that fit. Shop Now. Visit Virtual Showrooms explore Installation Get quick, convenient
Aluminum 6061-T6 has a minimum yield strength of 35 ksi (240 MPa), which is almost equal to that of A36 steel. This strength, combined with its light weight (about 1/3 that of steel), makes it particularly suitable for structural applications where static loads are a
Aluminum 6061-T6; 6061-T651. Subcategory: 6000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal. Close Analogs: Combines relatively high strength, good workability, and high resistance to corrosion; widely available. The T8 and T9 tempers offer better chipping characteristics over the T6
6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. ( 550 C) in a cooled die, leaving a part in W-temper condition before artificial aging to the T6 full strength state. Forgings. 6061 is an alloy
Two critical strength measures for 6061-T6 aluminum are yield strength and ultimate strength. The yield strength, which is the maximum stress the material can endure while remaining elastically deformed, is 276 MPa (40,000 psi). In comparison, the ultimate tensile strength, or the maximum stress the material can withstand before fracturing, is
This alloy is renowned for its excellent mechanical properties. 6061 T6 aluminum has a yield strength of 276 MPa, tensile strength of 310 MPa, and a shear strength of 207 MPa. Its elastic modulus is 68.9 GPa, with a fatigue strength of 96.5 MPa, Poisson\'s ratio of 0.33, and Brinell hardness of 95. The elongation at break ranges from 12 -
Tensile and Yield Strength: Aluminum 6061-T6 provides high tensile strength (approximay 310 MPa) and yield strength (around 276 MPa), making it ideal for load-bearing applications. Fatigue Strength: This alloy has a fatigue strength of about 96.5 MPa for 500 million cycles. For applications involving repeated stress, such as in aerospace
Aluminum 6061-T6 is the one of the most common types of aluminum metals used in the industrial world today. With its high strength-to-weight ratio and excellent mability, it is perfect for applications in aerospace, transportation equipment and construction materials manufacturing. Aluminum 6061-T6 is generally heat treated and
Aluminum 6061-T6; 6061-T651 Categories: Metal; Nonferrous Metal; Aluminum Alloy; 6000 Series Aluminum Alloy Material Tensile Strength, Ultimate 310 MPa 45000 psi AA; Typical 24.0 MPa Temperature 371 °C 3480 psi Temperature .0 MPa Temperature 316 °C 4640 psi Temperature 601
6061-T6 Alloy Aluminium Properties The below table outlines the material properties for 6061-T6 Alloy material including the young\'s modulus, yield strength, ultimate strength and other relevant mechanical properties required for structural and mechanical
6061-T6 aluminum is a heat-treated (T6 temper), high-strength alloy composed primarily of aluminum, magnesium, and silicon. Through quenching and artificial aging, it achieves remarkable hardness and strength, with key metrics including: Hardness: ≥ HB90. Tensile Compressive Strength: Up to 200. Shear Strength: 115